Primary Shaping – Powder Metallurgy Manufacturing Technology II Lecture 2 Laboratory for Machine Tools and Production Engineering Chair of Manufacturing Technology
Prof. Dr.-Ing. Dr.-Ing. E.h. F. Klocke
© WZL / IPT
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties Powder Compaction Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances Sizing Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 1
1
Structure of the lecture „Primary Shaping- Powder Metallurgy“ „ Introduction: Variety of Applications of Powder
Metallurgy
– Process Steps – Applications
Powder Production and Powder Properties Powder Compaction Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances Sizing Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 2
Process Steps of Powder Pressing
Powder
Lubricant
Mixing
Pressing
Sintering
Sizing
Graphite
Bronce Powder Iron Powder Alloyed Powder
© WZL / IPT
Seite 3
2
Application for Gear Boxes
source: Sinterstahl GmbH, Füssen © WZL / IPT
Seite 4
Applications in Automotive Engines
source: Sinterstahl GmbH, Füssen © WZL / IPT
Seite 5
3
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy „ Powder Production and Powder Properties – Powder Production Technologies – Powder Properties – Alloying Methods
Powder Compaction Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances Sizing Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 6
Powder Production: Chemical Reduction, Sponge Iron Powder 1 Reduction Mix of Coke Breeze and Limestone 2 Iron Ore 3 Drying 4 Crushing 5 Screening 6 Magnetic Separation 7 Charging in Ceramic Tubes 8 Reduction in Tunnel Kilns (1200°C) 9 Discharging 10 Coarse Crushing 11 Storage in Silos 12 Crushing 13 Magnetic Separation 14 Grinding and Screening 15 Annealing in Belt Furnace, approx. 800-900°C 16 Equalising 17 Automatic Packing 18 Iron Ore 19 Reduction Mix
source: Höganäs
© WZL / IPT
Seite 7
4
Powder Production: Water-Atomizing-Process „ Principle
„ Principle of Water-Atomizing
Atomizing the Melting by Means of Water Jet
1
„ Metal
2
Scrap, Iron Ore, Roll Scale
3 4
„ Factors of Influence Water Pressure
Melting Temperature
5
Flowrate of the Melting 1 2 3 4 5
Grain Size
„ Product
Foundry Ladle Melting Stream High Pressure Water Nozzle Atomized Iron Powder
Pure Iron or Alloy source: Höganäs, EHW Thale © WZL / IPT
Seite 8
Characterization of Iron and Steel Powder 1. Metallurgical Properties • Chemical Composition
⇒ Chemical Analysis
• Texture of Powder Particles
⇒ Polished Cross Sections
• Micro Hardness
⇒ Hardness Measurement
2. Geometrical Properties • Particle Size Distribution
⇒ Sieve Analysis
• External Practical Shape
⇒ Scanning Electron Microscopy
• Internal Particle Structure (Porosity) ⇒ Metallographic Cut through the Powder Particle 3. Mechanical Properties • Flow Rate
⇒ Hall-Flowmeter (Standardized Cone)
• Bulk Density
⇒ Filling a Bowl with a Standardized Cone
• Compressibility
⇒ Pressing Standardized Stopper, results presented as a curve
• Green Strength
⇒ Fatigue Strength of a Pressed Square Test Bar
• Spring-Back
⇒ Elastic Extension of a Pressed Stopper, d=25 mm
© WZL / IPT
Seite 9
5
Particle Form and – Structure of Unalloyed Iron Powder Scanning Electron Microscope-Picture
Cross Section
Sponge Iron Powder NC 100.24
Atomized Powder ASC 100.29
source: Höganäs © WZL / IPT
Seite 10
Alloying Methods of Iron Powders Completely Alloyed Powder
Mixed Alloyed Powder
Partially Alloyed Powder
© WZL / IPT
Seite 11
6
Alloying Methods of Iron Powders Completely Alloyed Powder
water-atomized powders, at which the molten material consists of the required alloying elements
Mixed Alloyed Powder
powder-mixes consisting of at least 2 pure alloying components
Partially Alloyed Powder
long sintering times and high sintering temperatures necessary for homogenizing diffusion alloyed: annealing of mixed powders adhesion alloyed: usage of alloying elements which can`t be bound on iron by a diffusion process
© WZL / IPT
Seite 12
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties „ Powder Compaction – – – –
Compendium Filling Pressing Ejection
Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances Sizing Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 13
7
The Compaction Cycle
© WZL / IPT
Seite 14
The Compaction Cycle Filling
Compacting
Ejecting
Upper Punch
Fill Shoe
Green Compact Compact
Green Compact
Die Lower Punch Powder © WZL / IPT
Green Compact Seite 15
8
Filling: Contour Filling Without contour filling
With Contour Filling
source: Osterwalder © WZL / IPT
Seite 16
Filling: Formation of Bridges when Filling Narrow Cross-Sections
Formation of bridges when filling narrow cross-sections
When high homogeneity requirements of the components: Pressed height of the component h < 15 mm: d > 2,5 mm Pressed height of the component h > 15 mm: d > h/6
© WZL / IPT
Seite 17
9
Compacting Pressure
Filling: Empirical Pressure-Density-Curve Defined at a Column of Powder 1000 MPa 600 400 200 3
Compacting Pressure [MPa]: Density [g/cm³]:
4
5
Compressed Density
6
[g/cm³]
7,86
0
80
200
400
800
2,5
4
5,5
6,5
7,2
© WZL / IPT
Seite 18
Pressing: Decreasing of the Axial Stress σa During Compaction Pa
Upper Punch Die Frictional forces at the wall of the compacting die restrain the compaction of The powder
σa(x) = σa(0) e -2µ/r
σα 0 F
With increasing distance from the face of the compacting punch, the axial stress σa, Which is available for the local densification of the powder, decreases.
source: Höganäs © WZL / IPT
f
K K
σa(x + dx) σa(x) σa(0)
x x + dx
2r
F = πr2 f = 2πrdx Seite 19
10
Pressing: Compacting Methods Used for the Production of Compacts One-Sided Compacting
Two-Sided Compacting
Compacting with Floating Die
© WZL / IPT
Seite 20
Pressing: Influence of the Density on the Material Properties m
1 + ν (ρ ) ρ P( ρ ) ρ = = 1 + ν 0 ρ0 P0 ρ0 ρ Density ρo Full Density P Material Properties Po Material Properties of the Raw Material m Powder Coefficient
m
Material Data
Powder Coefficient
Thermal Conductivity
1.5 … 3.5
Young’s Modulus
2.5 … 4.5
Dynamic Strength
3.5 … 5.5
Notched Impact Strength
>12
Material Data of the P/M-Steel: Distaloy HP-1: Fe-1.5Mo-4.0Ni-2.0Cu relativer RelativeWerkstoffkennwert Material Data P/P0P/P [-] 0 [-]
Calculation of Material Properties
1,0 .
. 0,8 Poisson’s Ratio 0,6 .
Young’s Modulus
0,4 .
Dynamic Strength 0,2 . 0,0 .
. 0,0
0,2 .
0,4 .
0,6 .
0,8 .
1,0 .
ρ/ρρ/ρ relative RelativeDichte Density 0 [-] 0 [-] © WZL / IPT
Seite 21
11
Ejection: Ejection Procedure Filling-Position Compaction-Position
Pressure-Relief
Upper Punch
Green Compact
Die
Powder
Bottom ram
Ejection-Position
Die Bolster
Bottom ram = ejector pin
© WZL / IPT
Seite 22
Withdrawal: Withdrawal Procedure Lifting
Compacting
Filling Upper Punch Powder
Compact
Die
Bottom Ram
Source: Fachverband für Pulvermetallurgie © WZL / IPT
Seite 23
12
Ejection: Schematic Diagramm of the Ejection Force Compact Die
Ejection Force
Bottom Ram
source: Höganäs
εel, punch
Punch Travel
© WZL / IPT
Seite 24
Ejection: Cracking Risk when Removing the Compact Crack Formation at the Compact Different elastic expansions of two lower punches
Ejection procedure at a sharp edge of the die
Dl1 Dl2
source: Höganäs © WZL / IPT
Avoiding crack formation by tapering the die exit and rounding-off the upper rim of the die! Seite 25
13
Ejection: Spring-Back as a Function of Compact Density
(λ
c
− λd ) λd
0,30
S: Spring-Back in % λc: Transversal Dimension of the (ejected) Compact λd: Corresponding Dimension of the Compacting Die (After Ejection of the Compact)
Spring-Back [%]
S(%) = 100 ⋅
0,20
Iron Powder with 0,8% Zn-Stearat as Lubricant Addition NC100.24 ASC100.29
0,10
„ Parameters Influencing the Spring-Back Compacting Pressure, Compacting Density, Powder Properties, Lubricants and Alloying Additions, 0,00 Shape & Elastic Properties of the Compacting Die
SC100.26
6,0
6,5
7,0
Compacting Density[g/cm³] source: Höganäs © WZL / IPT
Seite 26
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties Powder Compaction „ Constructions of Compaction Tools
Sintering – Basics and Examples of Sintering Furnances Sizing Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 27
14
Priciple of a Compaction Tool with a Split Die Filling
Component
Compacting
1 2 3 4
5 6 Opening 1 2 3 4 5 6
Lifting
Upper Punch Fill Shoe Upper Part of the Die, moveable Lower Part of the Die, fixed Bottom Rod Core Pin
source: Gräbener © WZL / IPT
Seite 28
Compaction Tool : Powder Compaction of Helical Gear Powder Compaction 1 Filling 2 Underfill by Die Lift 3 Closure of Die 4 Powder Transfer with Inner Punches 5 Compaction 6 Die Withdrawal with Upper Punch Hold Down Load
4
5
6
7
7 Full Demoulding by Inner Punch and Core Rod Withdrawal © WZL / IPT
Seite 29
15
Compaction Tool: Cross Hole and Complex Part with Different Filling Heights Compaction of a Part With a Cross Hole
Compaction of a Part with Different Filling Heights
source: Osterwalder © WZL / IPT
Seite 30
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties Powder Compaction Constructions of Compaction Tools „ Sintering – Basics and Examples of Sintering
Furnances Sizing Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 31
16
Temperature
Sintering: Different Atmospheres in a Sintering Conveyor Furnace °C
zone 1
zone 2 1120°C
1200 800
zone 3
zone 4
850°C
700°C
400
Room Temperature
150°C Smoke and Gas Outlet Gas Inlet
Zone 1: Burning-Off Lubricants
Zone 2: Sintering Zone 3:Re-Carbonizing
Zone 4:Cooling
Source: Höganäs © WZL / IPT
Seite 32
Sintering: Diffusion Types at Sintering Parameters Influencing the Diffusion:
a1
a2
„ Temperature „ Time „ Composition of Alloy
x1
l1
x2
l2
a1
a2
x2 > x1, l2 < l1 < 2a1, a2 ≤ a1,
Legend: v: Volume Diffusion s: Surface Diffusion b: Grain Boundary Diffusion e: Evaporation/Condensation : Forces from Surface Tension (viscous flow)
v
v
v
e b
source: Kuczynski © WZL / IPT
Seite 33
17
ρ
6,3 6,2
1150°C
850°C
15
1150°C
σB 10
Speciment: Standard Tension Test Bar
850°C
10 8 6 4 2 0
5
1150°C
δ
850°C 0 0
15
30
60
90
120
Elongation δ [%]
Density ρ Tensile Strength σB [kg/cm2] [g/cm3]
Sintering: Influence of Sinteing Time on the Material Properties
150
Sintering Time [min] © WZL / IPT
Seite 34
Different concepts of sintering furnaces
conveyor furnace
roller hearth furnace
pusher type furnace
walking-beam furnace
source: Höganäs © WZL / IPT
Seite 35
18
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties Powder Compaction Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances „ Sizing
Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 36
Sizing
Sizing involves reduction or increase in the dimensions of the component, and this action is performed by forcing the component into a die or over a core
• Hardness of the part to be sized should not exceed HV 180 after sintering • Wherever possible, the various surfaces of the part should be sized progressively and not simultaneously • The external forms should be sized before the holes in order to prevent cracking Quelle: Höganäs © WZL / IPT
Seite 37
19
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties Powder Compaction Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances Sizing „ Compendium of PM Manufacturing Technologies
Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 38
Process Sequences in PM-Technology 1 Powder Production Pouring
Pressureless Sintering
Sintering Sizing Oil Impregnation
High-Porous Components e.g.: Filters, Flam Traps, Throttles Quelle: GKN
Powder Production Compaction
Infiltration
Sintering
Pore Free Components
Infiltration Machining © WZL / IPT
Seite 39
20
Process Sequences in PM-Technology 2 Conventional Sintering
Warmcompaction Double Pressing
Powder Forging
Powder Production
Powder Production
Powder Production
Powder Production
Compaction
Compaction (150°C)
Compaction
Compaction
Sintering
Sintering
Sintering
Sintering
Sizing
Sizing
Re-Compaction
Inductional Heating
Heat Treatment
Heat Treatment
Re-Sintering
Forging
Machining
Machining
Sizing
Heat Treatment
Heat Treatment
Machining
Machining © WZL / IPT
Seite 40
PM Technology: Powder Forging Powder Forging Compaction Weight Control Sintering Inductive Heating Automatic Handling
Forging TForge> T Recristallisation Heat Treatment © WZL / IPT
Seite 41
21
PM Technology: Metal Injection Moulding MIM Metal Injection Moulding Powder:
Fe
Mixing
Grain Size: < 12 µm, Round Grain Form (Gas Atomised)
Pelleting
Highlights:
CHO
Extrude/ Inject
High Added Value Complex Geometry Component Mass: m < 500 g Thickness: s < 30mm, Debindering Time: t ~ s2 High Densities High Shrinkage
Debindering: Chemic / thermal
Sintering © WZL / IPT
Seite 42
PM Technology: MIM Applications Watchcase
Gearing parts
Medicine
1 2
Application: Synchronising Density: > 7,4 g/cm3 Heat Treat.: Case Hardening Tensile Strength: > 450 MPa Mass: ca. 28 g (1) ca. 6 g (2, 3)
3
Application: Watchcase G-Shock Material: Titan Alloy Density: 4,38 g/cm3 Waterproof up to 200m
Material:
Nickel Free, Stainless Steel Density: 7,6 g/cm3 Yield strength: 552 N/mm2 Tensile Strength: 657 N/mm2
Quelle: (1) GKN; (2) (3) © WZL / IPT
Seite 43
22
PM Technology: Isostatic Pressing Isostatic Compaction „ Up to 100% Density
Mould Filling
„ No Density Gradients „ Great Material Spectrum
Fluid Filling
„ Low Cycle Time
Applying Pressure
Fluid Discharge
Handling
1
2
3
Sintering © WZL / IPT
Seite 44
PM Technology: Isostatic Pressing
© WZL / IPT
Seite 45
23
PM Technology: Surface Densification by Transverse Rolling MBrems
ρges,0
MWalz FWalz
Process Conditions
Process Results
Workpiece: Initial Density: ρges,0 Gradient of Overmeasure: a(s) Tool: Tool Geometry Process: Transverse Rolling Force: FWalz ; Infeed: f Rolling: MWalz or Braking Torque: MBrems Number of Cycles: nÜ
Workpiece: Densification Gradient Densification Depth: tD,98% Gear Tooth Quality Tool: Load: F Stress: σ Deformation: ε
© WZL / IPT
Seite 46
PM Technology: Typical Deviations of Surface Densified P/M Gears Profile
„ Profile Deviation
Addendum
1.0 mm
– Positive Pressure Angle – Negative Crowning – Asymmetric Profile on the right and left Flank
20 µm
Tooth Root
left Flank „ Densification Defects
Workpiece
right Flank 1000 µm
– Incomplete Densification in Highly Loaded Areas – Asymmetric Densification on left and right Flank
Source: Höganäs AB © WZL / IPT
Seite 47
24
PM Technology: FE Model of Surface Densification by Rolling „ Objects – Rigid Tool – Rigid Shaft – Porous P/M Gear ƒ Number of Elements: 3374 ƒ Number of Nods: 3580 ƒ Weighted Mesh
MBrems
FW nWerkzeug
„ Interobject Conditions – Shaft - P/M-Gear: Sticking – Tool - P/M-Gear:
P/M gear Porous
„ Simulation Parameters – Step: ∆t = 0,0005s – Direct Method Iteration – Calculation Time: 6h/cycle
Tool Rigid Evaluated Pair of Teeth
Shaft Rigid
© WZL / IPT
Seite 48
PM Technology: Comparison of the Density Gradient determined through Simulation and Experiments „ Comparison of the
Metallographic Picture
1.000
1000 µm
– High Densification in the Addendum – Nonuniform Densification on the left and right Flank – Incomplete Densification on the right Flank – Nonuniform Densification of the right and left Tooth Root
0.976 0.952 0.928 0.904 Source: Höganäs AB
© WZL / IPT
FE Analysis Results
Relative Density ρ/ρ0 [-]
Density Gradient determined through Simulation and Experiments
0.880
Seite 49
25
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties Powder Compaction Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances Sizing Compendium of PM Manufacturing Technologies „ Comparison of the PM Manufacturing Technologies
Summary
© WZL / IPT
Seite 50
MIM
middle
Costs
high
Comparison: Production Costs
Double-Process Sintering
Powder Forging
low
Warm Compaction
7,2
7,4
Density [g/cm³] ( © WZL / IPT
Local Densification
Conventional Compaction
7,6
7,8
Strength) Seite 51
26
MIM
Warm Compaction Double Process Sintering
middle
high
Conventional Compaction
Powder Forging
Local Densification low
Geometry Complexity
Comparison: Geometrie Complexity
7,2
7,4
7,6
Density [g/cm³] (
7,8
Strength)
© WZL / IPT
Seite 52
Conventional Compaction
middle
Precision
high
Comparison: Precision Selective Densification Warm Compaction Double-Process Sintering
Powder Forging
low
MIM
7,2
7,4
Density [g/cm³] ( © WZL / IPT
7,6
7,8
Strength) Seite 53
27
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties Powder Compaction Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances Sizing Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies „ Summary
© WZL / IPT
Seite 54
Conclusion: Principle, Advantages and Limits of P/M Technology „ Advantages of P/M
Technology – Low Costs at Series Production – High Quality at Series Production – Net-Shape Technology – Extensive Alloying Possibilities – Weight Reduction Because of Porosity – 100% Raw Material Utilisation – Low Energy Consumption – Freedom in Profile Design „ Limits of P/M Technology
Proceeding of Single Process Sintering:
Powder
Mixing
Pressing
Sintering
Sizing
Sintered Components: Test Gear
Camshaft Gear
– Density Dependent Properties – Undercuts, Cross Holes and Thread not Producible by Pressing – Maximum Weight of Component 1 kg Source: Höganäs AB © WZL / IPT
Source: Miba AG Seite 55
28
Classification of sintered steels according to alloying elements The classification of sintered steels primarily acts upon the copper-content and the mass of the remaining alloying elements. e.g.: SINT D 30
with
SINT: character: 1st digit: 2nd digit:
sintered material density dependency material composition serial number
gear 0: 1: 2: 3:
Cu- Ni-alloy SINT-D 30 oil pump casing
4: 5: 6: 7:
sintered steel with percentage weight of 0% - 1% Cu, with or without C sintered steel with percentage weight of 1% - 5% Cu, with or without C sintered steel with percentage weight of more than 5% Cu, with or without C sintered steel with or without Cu, with or without C, but with a percentage weight of up to 6% of other alloying elements sintered steel with or without Cu, with or without C, but with a percentage weight of more than 6% of other alloying elements sintered alloys with a percentage weight of more than 60% Cu sintered metals which are not included in no. 5 sintered light metals, e.g. sintered aluminium
Cu-infiltrated SINT-F 22 © WZL / IPT
Seite 56
Classification of sintered steel according to porosity porosity P [%]
material class
sintered density ratio Rx [%]
SINT - AF
> 27
SINT - A
25 ± 2,5
75 ± 2,5
plain bearings
SINT - B
20 ± 2,5
80 ± 2,5
plain bearings, seals, guide rings. structural parts for low loads
SINT - C
15 ± 2,5
85 ± 2,5
plain bearings, sliding pats, medium-strength parts, e.g. shock absorber parts, oil pump gears
SINT - D
10 ± 2,5
90 ± 2,5
high-strength parts for high static and moderate dynamic loads
SINT - E
6±1,5
94 ± 1,5
high-strength parts for high static and high dynamic loads
SINT - F
<4,5
> 95,5
SINT - G
<8
> 92
with plastic or metal impregnated parts, high corrosion resistance, impermeable for oil and water
SINT - S
< 10
> 90
warm-compacted plain bearings and sliding elements with internal solid lubricant
© WZL / IPT
< 73
preferred applications
filter, flame traps, throttles
warm-compacted parts for highest loads
Seite 57
29
Tolerances of different shaping processes Process
ISO-Quality IT
5
6
7
8
9
10
11
12
13
14
15
16 diameter tolerances
conventional PM-technology powder forging conventional PM-technology with sizing investment casting diecasting forming under compressive conditions, hot extrusion warm working extrusion cold extrusion turning cylindrical grinding
All tolerances are rough values and depend on the size of the components and on the material!
© WZL / IPT
Seite 58
Catalogue of questions to summarize the lecture „Powder metallurgy“ Explain the two significant methods for powder production, the methods for the characterization of metal powders and the three different alloying techniques! Sketch the phases of compaction (use a cylindrical compact)! ¾
Explain the density distribution, ejection force and spring-back!
¾
Explain an industrial sintering process on the basis of a sintering conveyor furnace!
¾
Explain the reasons for a sizing operation! Explain then a sizing operation, as example use e.g. the ball sizing of bushes !
¾
Specify and explain the schematic flow of conventional PM-processes!
¾
Which possibilities are provided by PM-technology for producing highly loaded parts?
¾
Specify and explain the influencing parameters on the produciton costs of PM-parts!
© WZL / IPT
Seite 59
30
Prof. Dr.-Ing. Dr.-Ing. E.h. F. Klocke
© WZL / IPT
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties Powder Compaction Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances Sizing Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 1
1
Structure of the lecture „Primary Shaping- Powder Metallurgy“ „ Introduction: Variety of Applications of Powder
Metallurgy
– Process Steps – Applications
Powder Production and Powder Properties Powder Compaction Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances Sizing Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 2
Process Steps of Powder Pressing
Powder
Lubricant
Mixing
Pressing
Sintering
Sizing
Graphite
Bronce Powder Iron Powder Alloyed Powder
© WZL / IPT
Seite 3
2
Application for Gear Boxes
source: Sinterstahl GmbH, Füssen © WZL / IPT
Seite 4
Applications in Automotive Engines
source: Sinterstahl GmbH, Füssen © WZL / IPT
Seite 5
3
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy „ Powder Production and Powder Properties – Powder Production Technologies – Powder Properties – Alloying Methods
Powder Compaction Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances Sizing Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 6
Powder Production: Chemical Reduction, Sponge Iron Powder 1 Reduction Mix of Coke Breeze and Limestone 2 Iron Ore 3 Drying 4 Crushing 5 Screening 6 Magnetic Separation 7 Charging in Ceramic Tubes 8 Reduction in Tunnel Kilns (1200°C) 9 Discharging 10 Coarse Crushing 11 Storage in Silos 12 Crushing 13 Magnetic Separation 14 Grinding and Screening 15 Annealing in Belt Furnace, approx. 800-900°C 16 Equalising 17 Automatic Packing 18 Iron Ore 19 Reduction Mix
source: Höganäs
© WZL / IPT
Seite 7
4
Powder Production: Water-Atomizing-Process „ Principle
„ Principle of Water-Atomizing
Atomizing the Melting by Means of Water Jet
1
„ Metal
2
Scrap, Iron Ore, Roll Scale
3 4
„ Factors of Influence Water Pressure
Melting Temperature
5
Flowrate of the Melting 1 2 3 4 5
Grain Size
„ Product
Foundry Ladle Melting Stream High Pressure Water Nozzle Atomized Iron Powder
Pure Iron or Alloy source: Höganäs, EHW Thale © WZL / IPT
Seite 8
Characterization of Iron and Steel Powder 1. Metallurgical Properties • Chemical Composition
⇒ Chemical Analysis
• Texture of Powder Particles
⇒ Polished Cross Sections
• Micro Hardness
⇒ Hardness Measurement
2. Geometrical Properties • Particle Size Distribution
⇒ Sieve Analysis
• External Practical Shape
⇒ Scanning Electron Microscopy
• Internal Particle Structure (Porosity) ⇒ Metallographic Cut through the Powder Particle 3. Mechanical Properties • Flow Rate
⇒ Hall-Flowmeter (Standardized Cone)
• Bulk Density
⇒ Filling a Bowl with a Standardized Cone
• Compressibility
⇒ Pressing Standardized Stopper, results presented as a curve
• Green Strength
⇒ Fatigue Strength of a Pressed Square Test Bar
• Spring-Back
⇒ Elastic Extension of a Pressed Stopper, d=25 mm
© WZL / IPT
Seite 9
5
Particle Form and – Structure of Unalloyed Iron Powder Scanning Electron Microscope-Picture
Cross Section
Sponge Iron Powder NC 100.24
Atomized Powder ASC 100.29
source: Höganäs © WZL / IPT
Seite 10
Alloying Methods of Iron Powders Completely Alloyed Powder
Mixed Alloyed Powder
Partially Alloyed Powder
© WZL / IPT
Seite 11
6
Alloying Methods of Iron Powders Completely Alloyed Powder
water-atomized powders, at which the molten material consists of the required alloying elements
Mixed Alloyed Powder
powder-mixes consisting of at least 2 pure alloying components
Partially Alloyed Powder
long sintering times and high sintering temperatures necessary for homogenizing diffusion alloyed: annealing of mixed powders adhesion alloyed: usage of alloying elements which can`t be bound on iron by a diffusion process
© WZL / IPT
Seite 12
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties „ Powder Compaction – – – –
Compendium Filling Pressing Ejection
Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances Sizing Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 13
7
The Compaction Cycle
© WZL / IPT
Seite 14
The Compaction Cycle Filling
Compacting
Ejecting
Upper Punch
Fill Shoe
Green Compact Compact
Green Compact
Die Lower Punch Powder © WZL / IPT
Green Compact Seite 15
8
Filling: Contour Filling Without contour filling
With Contour Filling
source: Osterwalder © WZL / IPT
Seite 16
Filling: Formation of Bridges when Filling Narrow Cross-Sections
Formation of bridges when filling narrow cross-sections
When high homogeneity requirements of the components: Pressed height of the component h < 15 mm: d > 2,5 mm Pressed height of the component h > 15 mm: d > h/6
© WZL / IPT
Seite 17
9
Compacting Pressure
Filling: Empirical Pressure-Density-Curve Defined at a Column of Powder 1000 MPa 600 400 200 3
Compacting Pressure [MPa]: Density [g/cm³]:
4
5
Compressed Density
6
[g/cm³]
7,86
0
80
200
400
800
2,5
4
5,5
6,5
7,2
© WZL / IPT
Seite 18
Pressing: Decreasing of the Axial Stress σa During Compaction Pa
Upper Punch Die Frictional forces at the wall of the compacting die restrain the compaction of The powder
σa(x) = σa(0) e -2µ/r
σα 0 F
With increasing distance from the face of the compacting punch, the axial stress σa, Which is available for the local densification of the powder, decreases.
source: Höganäs © WZL / IPT
f
K K
σa(x + dx) σa(x) σa(0)
x x + dx
2r
F = πr2 f = 2πrdx Seite 19
10
Pressing: Compacting Methods Used for the Production of Compacts One-Sided Compacting
Two-Sided Compacting
Compacting with Floating Die
© WZL / IPT
Seite 20
Pressing: Influence of the Density on the Material Properties m
1 + ν (ρ ) ρ P( ρ ) ρ = = 1 + ν 0 ρ0 P0 ρ0 ρ Density ρo Full Density P Material Properties Po Material Properties of the Raw Material m Powder Coefficient
m
Material Data
Powder Coefficient
Thermal Conductivity
1.5 … 3.5
Young’s Modulus
2.5 … 4.5
Dynamic Strength
3.5 … 5.5
Notched Impact Strength
>12
Material Data of the P/M-Steel: Distaloy HP-1: Fe-1.5Mo-4.0Ni-2.0Cu relativer RelativeWerkstoffkennwert Material Data P/P0P/P [-] 0 [-]
Calculation of Material Properties
1,0 .
. 0,8 Poisson’s Ratio 0,6 .
Young’s Modulus
0,4 .
Dynamic Strength 0,2 . 0,0 .
. 0,0
0,2 .
0,4 .
0,6 .
0,8 .
1,0 .
ρ/ρρ/ρ relative RelativeDichte Density 0 [-] 0 [-] © WZL / IPT
Seite 21
11
Ejection: Ejection Procedure Filling-Position Compaction-Position
Pressure-Relief
Upper Punch
Green Compact
Die
Powder
Bottom ram
Ejection-Position
Die Bolster
Bottom ram = ejector pin
© WZL / IPT
Seite 22
Withdrawal: Withdrawal Procedure Lifting
Compacting
Filling Upper Punch Powder
Compact
Die
Bottom Ram
Source: Fachverband für Pulvermetallurgie © WZL / IPT
Seite 23
12
Ejection: Schematic Diagramm of the Ejection Force Compact Die
Ejection Force
Bottom Ram
source: Höganäs
εel, punch
Punch Travel
© WZL / IPT
Seite 24
Ejection: Cracking Risk when Removing the Compact Crack Formation at the Compact Different elastic expansions of two lower punches
Ejection procedure at a sharp edge of the die
Dl1 Dl2
source: Höganäs © WZL / IPT
Avoiding crack formation by tapering the die exit and rounding-off the upper rim of the die! Seite 25
13
Ejection: Spring-Back as a Function of Compact Density
(λ
c
− λd ) λd
0,30
S: Spring-Back in % λc: Transversal Dimension of the (ejected) Compact λd: Corresponding Dimension of the Compacting Die (After Ejection of the Compact)
Spring-Back [%]
S(%) = 100 ⋅
0,20
Iron Powder with 0,8% Zn-Stearat as Lubricant Addition NC100.24 ASC100.29
0,10
„ Parameters Influencing the Spring-Back Compacting Pressure, Compacting Density, Powder Properties, Lubricants and Alloying Additions, 0,00 Shape & Elastic Properties of the Compacting Die
SC100.26
6,0
6,5
7,0
Compacting Density[g/cm³] source: Höganäs © WZL / IPT
Seite 26
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties Powder Compaction „ Constructions of Compaction Tools
Sintering – Basics and Examples of Sintering Furnances Sizing Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 27
14
Priciple of a Compaction Tool with a Split Die Filling
Component
Compacting
1 2 3 4
5 6 Opening 1 2 3 4 5 6
Lifting
Upper Punch Fill Shoe Upper Part of the Die, moveable Lower Part of the Die, fixed Bottom Rod Core Pin
source: Gräbener © WZL / IPT
Seite 28
Compaction Tool : Powder Compaction of Helical Gear Powder Compaction 1 Filling 2 Underfill by Die Lift 3 Closure of Die 4 Powder Transfer with Inner Punches 5 Compaction 6 Die Withdrawal with Upper Punch Hold Down Load
4
5
6
7
7 Full Demoulding by Inner Punch and Core Rod Withdrawal © WZL / IPT
Seite 29
15
Compaction Tool: Cross Hole and Complex Part with Different Filling Heights Compaction of a Part With a Cross Hole
Compaction of a Part with Different Filling Heights
source: Osterwalder © WZL / IPT
Seite 30
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties Powder Compaction Constructions of Compaction Tools „ Sintering – Basics and Examples of Sintering
Furnances Sizing Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 31
16
Temperature
Sintering: Different Atmospheres in a Sintering Conveyor Furnace °C
zone 1
zone 2 1120°C
1200 800
zone 3
zone 4
850°C
700°C
400
Room Temperature
150°C Smoke and Gas Outlet Gas Inlet
Zone 1: Burning-Off Lubricants
Zone 2: Sintering Zone 3:Re-Carbonizing
Zone 4:Cooling
Source: Höganäs © WZL / IPT
Seite 32
Sintering: Diffusion Types at Sintering Parameters Influencing the Diffusion:
a1
a2
„ Temperature „ Time „ Composition of Alloy
x1
l1
x2
l2
a1
a2
x2 > x1, l2 < l1 < 2a1, a2 ≤ a1,
Legend: v: Volume Diffusion s: Surface Diffusion b: Grain Boundary Diffusion e: Evaporation/Condensation : Forces from Surface Tension (viscous flow)
v
v
v
e b
source: Kuczynski © WZL / IPT
Seite 33
17
ρ
6,3 6,2
1150°C
850°C
15
1150°C
σB 10
Speciment: Standard Tension Test Bar
850°C
10 8 6 4 2 0
5
1150°C
δ
850°C 0 0
15
30
60
90
120
Elongation δ [%]
Density ρ Tensile Strength σB [kg/cm2] [g/cm3]
Sintering: Influence of Sinteing Time on the Material Properties
150
Sintering Time [min] © WZL / IPT
Seite 34
Different concepts of sintering furnaces
conveyor furnace
roller hearth furnace
pusher type furnace
walking-beam furnace
source: Höganäs © WZL / IPT
Seite 35
18
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties Powder Compaction Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances „ Sizing
Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 36
Sizing
Sizing involves reduction or increase in the dimensions of the component, and this action is performed by forcing the component into a die or over a core
• Hardness of the part to be sized should not exceed HV 180 after sintering • Wherever possible, the various surfaces of the part should be sized progressively and not simultaneously • The external forms should be sized before the holes in order to prevent cracking Quelle: Höganäs © WZL / IPT
Seite 37
19
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties Powder Compaction Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances Sizing „ Compendium of PM Manufacturing Technologies
Comparison of the PM Manufacturing Technologies Summary
© WZL / IPT
Seite 38
Process Sequences in PM-Technology 1 Powder Production Pouring
Pressureless Sintering
Sintering Sizing Oil Impregnation
High-Porous Components e.g.: Filters, Flam Traps, Throttles Quelle: GKN
Powder Production Compaction
Infiltration
Sintering
Pore Free Components
Infiltration Machining © WZL / IPT
Seite 39
20
Process Sequences in PM-Technology 2 Conventional Sintering
Warmcompaction Double Pressing
Powder Forging
Powder Production
Powder Production
Powder Production
Powder Production
Compaction
Compaction (150°C)
Compaction
Compaction
Sintering
Sintering
Sintering
Sintering
Sizing
Sizing
Re-Compaction
Inductional Heating
Heat Treatment
Heat Treatment
Re-Sintering
Forging
Machining
Machining
Sizing
Heat Treatment
Heat Treatment
Machining
Machining © WZL / IPT
Seite 40
PM Technology: Powder Forging Powder Forging Compaction Weight Control Sintering Inductive Heating Automatic Handling
Forging TForge> T Recristallisation Heat Treatment © WZL / IPT
Seite 41
21
PM Technology: Metal Injection Moulding MIM Metal Injection Moulding Powder:
Fe
Mixing
Grain Size: < 12 µm, Round Grain Form (Gas Atomised)
Pelleting
Highlights:
CHO
Extrude/ Inject
High Added Value Complex Geometry Component Mass: m < 500 g Thickness: s < 30mm, Debindering Time: t ~ s2 High Densities High Shrinkage
Debindering: Chemic / thermal
Sintering © WZL / IPT
Seite 42
PM Technology: MIM Applications Watchcase
Gearing parts
Medicine
1 2
Application: Synchronising Density: > 7,4 g/cm3 Heat Treat.: Case Hardening Tensile Strength: > 450 MPa Mass: ca. 28 g (1) ca. 6 g (2, 3)
3
Application: Watchcase G-Shock Material: Titan Alloy Density: 4,38 g/cm3 Waterproof up to 200m
Material:
Nickel Free, Stainless Steel Density: 7,6 g/cm3 Yield strength: 552 N/mm2 Tensile Strength: 657 N/mm2
Quelle: (1) GKN; (2) (3) © WZL / IPT
Seite 43
22
PM Technology: Isostatic Pressing Isostatic Compaction „ Up to 100% Density
Mould Filling
„ No Density Gradients „ Great Material Spectrum
Fluid Filling
„ Low Cycle Time
Applying Pressure
Fluid Discharge
Handling
1
2
3
Sintering © WZL / IPT
Seite 44
PM Technology: Isostatic Pressing
© WZL / IPT
Seite 45
23
PM Technology: Surface Densification by Transverse Rolling MBrems
ρges,0
MWalz FWalz
Process Conditions
Process Results
Workpiece: Initial Density: ρges,0 Gradient of Overmeasure: a(s) Tool: Tool Geometry Process: Transverse Rolling Force: FWalz ; Infeed: f Rolling: MWalz or Braking Torque: MBrems Number of Cycles: nÜ
Workpiece: Densification Gradient Densification Depth: tD,98% Gear Tooth Quality Tool: Load: F Stress: σ Deformation: ε
© WZL / IPT
Seite 46
PM Technology: Typical Deviations of Surface Densified P/M Gears Profile
„ Profile Deviation
Addendum
1.0 mm
– Positive Pressure Angle – Negative Crowning – Asymmetric Profile on the right and left Flank
20 µm
Tooth Root
left Flank „ Densification Defects
Workpiece
right Flank 1000 µm
– Incomplete Densification in Highly Loaded Areas – Asymmetric Densification on left and right Flank
Source: Höganäs AB © WZL / IPT
Seite 47
24
PM Technology: FE Model of Surface Densification by Rolling „ Objects – Rigid Tool – Rigid Shaft – Porous P/M Gear ƒ Number of Elements: 3374 ƒ Number of Nods: 3580 ƒ Weighted Mesh
MBrems
FW nWerkzeug
„ Interobject Conditions – Shaft - P/M-Gear: Sticking – Tool - P/M-Gear:
P/M gear Porous
„ Simulation Parameters – Step: ∆t = 0,0005s – Direct Method Iteration – Calculation Time: 6h/cycle
Tool Rigid Evaluated Pair of Teeth
Shaft Rigid
© WZL / IPT
Seite 48
PM Technology: Comparison of the Density Gradient determined through Simulation and Experiments „ Comparison of the
Metallographic Picture
1.000
1000 µm
– High Densification in the Addendum – Nonuniform Densification on the left and right Flank – Incomplete Densification on the right Flank – Nonuniform Densification of the right and left Tooth Root
0.976 0.952 0.928 0.904 Source: Höganäs AB
© WZL / IPT
FE Analysis Results
Relative Density ρ/ρ0 [-]
Density Gradient determined through Simulation and Experiments
0.880
Seite 49
25
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties Powder Compaction Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances Sizing Compendium of PM Manufacturing Technologies „ Comparison of the PM Manufacturing Technologies
Summary
© WZL / IPT
Seite 50
MIM
middle
Costs
high
Comparison: Production Costs
Double-Process Sintering
Powder Forging
low
Warm Compaction
7,2
7,4
Density [g/cm³] ( © WZL / IPT
Local Densification
Conventional Compaction
7,6
7,8
Strength) Seite 51
26
MIM
Warm Compaction Double Process Sintering
middle
high
Conventional Compaction
Powder Forging
Local Densification low
Geometry Complexity
Comparison: Geometrie Complexity
7,2
7,4
7,6
Density [g/cm³] (
7,8
Strength)
© WZL / IPT
Seite 52
Conventional Compaction
middle
Precision
high
Comparison: Precision Selective Densification Warm Compaction Double-Process Sintering
Powder Forging
low
MIM
7,2
7,4
Density [g/cm³] ( © WZL / IPT
7,6
7,8
Strength) Seite 53
27
Structure of the lecture „Primary Shaping- Powder Metallurgy“ Introduction: Variety of Applications of Powder Metallurgy Powder Production and Powder Properties Powder Compaction Constructions of Compaction Tools Sintering – Basics and Examples of Sintering Furnances Sizing Compendium of PM Manufacturing Technologies Comparison of the PM Manufacturing Technologies „ Summary
© WZL / IPT
Seite 54
Conclusion: Principle, Advantages and Limits of P/M Technology „ Advantages of P/M
Technology – Low Costs at Series Production – High Quality at Series Production – Net-Shape Technology – Extensive Alloying Possibilities – Weight Reduction Because of Porosity – 100% Raw Material Utilisation – Low Energy Consumption – Freedom in Profile Design „ Limits of P/M Technology
Proceeding of Single Process Sintering:
Powder
Mixing
Pressing
Sintering
Sizing
Sintered Components: Test Gear
Camshaft Gear
– Density Dependent Properties – Undercuts, Cross Holes and Thread not Producible by Pressing – Maximum Weight of Component 1 kg Source: Höganäs AB © WZL / IPT
Source: Miba AG Seite 55
28
Classification of sintered steels according to alloying elements The classification of sintered steels primarily acts upon the copper-content and the mass of the remaining alloying elements. e.g.: SINT D 30
with
SINT: character: 1st digit: 2nd digit:
sintered material density dependency material composition serial number
gear 0: 1: 2: 3:
Cu- Ni-alloy SINT-D 30 oil pump casing
4: 5: 6: 7:
sintered steel with percentage weight of 0% - 1% Cu, with or without C sintered steel with percentage weight of 1% - 5% Cu, with or without C sintered steel with percentage weight of more than 5% Cu, with or without C sintered steel with or without Cu, with or without C, but with a percentage weight of up to 6% of other alloying elements sintered steel with or without Cu, with or without C, but with a percentage weight of more than 6% of other alloying elements sintered alloys with a percentage weight of more than 60% Cu sintered metals which are not included in no. 5 sintered light metals, e.g. sintered aluminium
Cu-infiltrated SINT-F 22 © WZL / IPT
Seite 56
Classification of sintered steel according to porosity porosity P [%]
material class
sintered density ratio Rx [%]
SINT - AF
> 27
SINT - A
25 ± 2,5
75 ± 2,5
plain bearings
SINT - B
20 ± 2,5
80 ± 2,5
plain bearings, seals, guide rings. structural parts for low loads
SINT - C
15 ± 2,5
85 ± 2,5
plain bearings, sliding pats, medium-strength parts, e.g. shock absorber parts, oil pump gears
SINT - D
10 ± 2,5
90 ± 2,5
high-strength parts for high static and moderate dynamic loads
SINT - E
6±1,5
94 ± 1,5
high-strength parts for high static and high dynamic loads
SINT - F
<4,5
> 95,5
SINT - G
<8
> 92
with plastic or metal impregnated parts, high corrosion resistance, impermeable for oil and water
SINT - S
< 10
> 90
warm-compacted plain bearings and sliding elements with internal solid lubricant
© WZL / IPT
< 73
preferred applications
filter, flame traps, throttles
warm-compacted parts for highest loads
Seite 57
29
Tolerances of different shaping processes Process
ISO-Quality IT
5
6
7
8
9
10
11
12
13
14
15
16 diameter tolerances
conventional PM-technology powder forging conventional PM-technology with sizing investment casting diecasting forming under compressive conditions, hot extrusion warm working extrusion cold extrusion turning cylindrical grinding
All tolerances are rough values and depend on the size of the components and on the material!
© WZL / IPT
Seite 58
Catalogue of questions to summarize the lecture „Powder metallurgy“ Explain the two significant methods for powder production, the methods for the characterization of metal powders and the three different alloying techniques! Sketch the phases of compaction (use a cylindrical compact)! ¾
Explain the density distribution, ejection force and spring-back!
¾
Explain an industrial sintering process on the basis of a sintering conveyor furnace!
¾
Explain the reasons for a sizing operation! Explain then a sizing operation, as example use e.g. the ball sizing of bushes !
¾
Specify and explain the schematic flow of conventional PM-processes!
¾
Which possibilities are provided by PM-technology for producing highly loaded parts?
¾
Specify and explain the influencing parameters on the produciton costs of PM-parts!
© WZL / IPT
Seite 59
30
Related Documents 3m3m1z
Powder Metallurgy ph3m
April 2022 0
Principles Of Powder Metallurgy 6j1o2
December 2021 0
Powder Metallurgy Technology-ppt 1p4e
December 2019 62
Powder Metallurgy Project.ppt 3z3gc
April 2021 0
Mt Powder Metallurgy 5l4e56
April 2022 0